  • Product Name: S2(n) Halogen Free Thin Wall Cross-linked Polyolefin for General Purpose
  • Color: Standard color : Red,Blue, Yellow, Green, Black, Clear.
  • Temperature: Operating temperature: -40~125 ℃;Shrink temperature: 125 ℃.
    • Icon: Icon1 Icon2 Icon3 Icon4 Icon5 Icon6 Icon7

 

 Features:
   Insulation, Protection,Identification;      Flame retardant ;
   Halogen free, Flexible ;      Wide range of colors  ;
   Shrink Ratio:2:1 & 3:1;     Voltage Class:600~1000 V.
 Typical application:
   Ideal for electrical insulation,strain relief,wire bonding and light harness jacketing;
   Common applications include electronic systems of subway, aircraft, submarine, control room facilities and sealed environment
 Approvals:
  UL approval;     File No.:
 Cross reference:
  Raychem/Tyco : Versafit V2 / RNF-100.
 

Dimensions

Shrink ratio 2:1

Reference As supplied ID (mm) After recovered(mm) Standard length Reference As supplied ID(mm) After recovered(mm) Standard length
UPM S2(n) ID max. WT  m/spool UPM S2(n) ID max. WT  m/spool
0.6 0.9±0.2 0.4 0.33±0.10 200 15.0 15.5±0.4 7.5 0.70±0.10 100
0.8 1.1±0.2 0.5 0.33±0.10 200 16.0 16.5±0.4 8.0 0.70±0.10 100
1.0 1.5±0.2 0.7 0.36±0.10 200 17.0 17.5±0.4 8.5 0.70±0.10 100
1.5 2.0±0.2 0.9 0.45±0.10 200 18.0 19.0±0.5 9.0 0.70±0.10 100
2.0 2.5±0.2 1.0 0.45±0.10 200 20.0 22.0±0.5 10.0 0.80±0.15 100
2.5 3.0±0.2 1.3 0.45±0.10 200 22.0 24.0±0.5 11.0 0.80±0.15 100
3.0 3.5±0.2 1.5 0.45±0.10 200 25.0 26.0±0.5 12.5 0.90±0.15 50
3.5 4.0±0.2 1.8 0.45±0.10 200 28.0 29.0±0.5 14.0 0.90±0.15 50
4.0 4.5±0.2 2.0 0.45±0.10 200 30.0 31.5±1.0 15.0 1.00±0.15 50
4.5 5.0±0.2 2.3 0.45±0.10 100 35.0 36.5±1.0 17.5 1.00±0.15 50
5.0 5.5±0.2 2.5 0.56±0.10 100 40.0 41.5±1.0 20.0 1.00±0.15 50
5.5 6.0±0.2 2.8 0.56±0.10 100 45.0 ≥45 22.5 1.10±0.15 25
6.0 6.5±0.2 3.0 0.56±0.10 100 50.0 ≥50 25.0 1.10±0.15 25
7.0 7.5±0.3 3.5 0.56±0.10 100 60.0 ≥60 31.0 1.20±0.20 25
8.0 8.5±0.3 4.0 0.56±0.10 100 70.0 ≥70 36.0 1.20±0.20 25
9.0 9.5±0.3 4.5 0.56±0.10 100 80.0 ≥80 41.0 1.30±0.20 25
10.0 10.5±0.3 5.0 0.56±0.10 100 90.0 ≥90 46.0 1.30±0.20 25
11.0 11.5±0.3 5.5 0.56±0.10 100 100.0 ≥100 51.0 1.30±0.20 25
12.0 12.5±0.3 6.0 0.56±0.10 100 120.0 ≥120 61.0 1.30±0.20 25
13.0 13.5±0.3 6.5 0.70±0.10 100 150.0 ≥150 76.0 1.30±0.20 25
14.0 14.5±0.3 7.0 0.70±0.10 100 180.0 ≥180 91.0 1.30±0.20 25

Shrink ratio 3:1

Reference As supplied(mm) After recovered(mm) Standard length
UPM S2(n) ID min. ID max. WT nom. m
1.5/0.5 1.5 0.5 0.5 200
3.0/1.0 3.0 1.0 0.7 200
4.5/1.5 4.5 1.5 0.7 100
6/2 6.0 2.0 0.8 100
9/3 9.0 3.0 1.0 50
12/4 12.0 4.0 1.1 50
15/5 15.0 5.0 1.2 50
18/6 18.0 6.0 1.3 50
24/8 24.0 8.0 1.5 25
30/10 30.0 10.0 1.7 25
39/13 39.0 13.0 1.9 25
50/16 50.0 16.0 2.5 1
60/20 60.0 20.0 2.6 1
70/23 70.0 23.0 2.6 1
80/26 80.0 26.0 2.8 1
90/30 90.0 30.0 2.8 1
100/33 100.0 33.0 3.0 1

      ID=Internal Diameter                    WT= wall thickness

 

     

Property Test Method Values
Physical Density -- 1.25~1.35
  Thermal endurance -- 125℃
  Tensile strength When test at 500mm/min. ≥10.4 MPa
  Breakdown elongation When test at 500mm/min. ≥ 200%
Aging(158 ℃/168hrs)   Tensile strength When test at 500mm/min. ≥ 7.3 MPa
Breakdown elongation When test at 500mm/min. ≥ 100%
  Heat shock 4hrs. at 250℃ No cracking,
drop or flow
  Cold bend  1 hour at -30℃ No cracking
                    Water absorption 24h at 23℃ -- ≤0.5%
  Halogen free  IEC 61249-2-21 Cl:900ppm max. Br:900ppm max.Total (Cl + Br) : 1500ppm max.
 

Electrical


Dielectric  breakdown voltage.


--


≥ AC 2500V

  Dielectric voltage Withstand    1min.AC2500V No breakdown
  Aging(158 ℃/168hrs)   Dielectric  breakdown voltage -- AC 2500V min. and more than 50% of the value obtained with unaged sample
Dielectric voltage Withstand  1min.AC2500V No breakdown
  Volume resistivity -- ≥1014 Ω.cm

Chemical 


Copper stability 


168h at 158℃ 500mm/min.


Elongation≥100%

  Flammability All Tubing Test UL224

   

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

Note: The test methods conform to UL224.